Bambu PETG-CF is a composite material consisting of PETG and carbon fiber. The new formula greatly improved printing quality by reducing clumping compared to traditional PETG. With the addition of carbon fiber, Bambu PETG-CF offers improved strength while maintaining good toughness and a shiny look. It is an ideal material for drone parts, racing models, and various functional parts that require both high performance, especially impact strength, and a sleek appearance.
Bambu PETG-CF is improved with a modified formula that specifically addresses the issue of clumping and sticking to nozzle during PETG printing.
Carbon fiber brings advanced texture to the print surface, while retaining the shine of PETG itself.
Carbon fiber brings soft reflection, minimal layer lines and a unique delicate texture.
Different from PLA-CF's matte finish, PETG-CF offers a shiny finish and thus one more choice.
The addition of carbon fiber also significantly enhances the XY strength of PETG without sacrificing layer bonding.
Learn more different filaments comparison on Bambu Filament Guide >>
| PLA-CF | PETG-CF | |
| Price | $34.99 | $34.99 |
| Filament Type | Carbon Fiber Infill | Carbon Fiber Infill |
| Hotend Compatibility | Hotend with Hardened Steel Nozzle 0.4 mm / 0.6 mm / 0.8 mm | Hotend with Hardened Steel Nozzle 0.4 mm / 0.6 mm / 0.8 mm |
| Build Plate Compatibility | Cool Plate SuperTack, Smooth PEI Plate, Textured PEI Plate | Cool Plate SuperTack, Smooth PEI Plate, Textured PEI Plate |
| AMS Compatibility | Yes | Yes |
| Surface | Matte | Shiny |
| Print Speed | <250 mm/s | <200 mm/s |
| Toughness (Impact Strength - XY) | 23.2 kJ/m² | 41.2 kJ/m² |
| Strength (Bending Strength - XY) | 89 MPa | 70 MPa |
| Stiffness (Bending Modulus - XY) | 3950 MPa | 2910 MPa |
| Layer Adhesion (Impact Strength - Z) | 7.8 kJ/m² | 10.7 kJ/m² |
| Heat Resistant（HDT, 0.45 MPa） | 55 °C | 74 °C |
Compared to other carbon fiber materials, Bambu PETG-CF exhibits exceptional toughness
and is less prone to fracture under external stress and impact.
| Recommended | Not Recommended | |
| Build Plate | Cool Plate SuperTack, Smooth PEI Plate, Textured PEI Plate | / |
| Hotend | Hotend with Hardened Steel Nozzle 0.4 mm / 0.6 mm / 0.8 mm | Hotend with Stainless Steel Nozzle All Size |
| Glue | Bambu Liquid Glue Glue Stick |
/ |
| Color | Hex Code | Display |
| Brick Red | #9f332a | |
| Violet Purple | #583061 | |
| Indigo Blue | #324585 | |
| Malachite Green | #16b08e | |
| Black | #000000 | |
| Titan Gray | #565656 |
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System).
Load and print! No more tedious setting steps.
| Recommended Printing Settings | |
| Drying Settings (Blast Drying Oven) | 65 °C，8 h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 240 - 270 °C |
| Bed Temperature (with Glue) | 65 - 75 °C |
| Printing Speed | < 200 mm/s |
| Physical Properties | |
| Density | 1.25 g/cm³ |
| Vicat Softening Temperature | 85 °C |
| Heat Deflection Temperature | 74 °C |
| Melting Temperature | 225 °C |
| Melt Index | 19.3 ± 2.4 g/10 min |
| Mechanical Properties | |
| Tensile Strength | 35 ± 5 MPa |
| Breaking Elongation Rate | 10.4 ± 0.6 % |
| Bending Modulus | 2910 ± 260 MPa |
| Bending Strength | 70 ± 5 MPa |
| Impact Strength | 41.2 ± 2.6 kJ/m² |
• Bambu PETG-CF needs proper drying before printing. Drying conditions: 65 ℃ for 8 hrs. Store in a dry environment after use. Dry before use if the material absorbs moisture. For more details please refer to: Filament drying instructions on WIKI.
• To get stronger Z-adhesion, please set a higher infill density, and do not use an open-frame printer or set too large fan percentages to avoid over cooling.
• To get shinier looks, set lower speeds and relatively higher temperatures.