PA6-CF

Carbon Fiber Reinforced PA6 (Nylon 6)

$42.99 USD

Product Features
  • Superior Strength and Stiffness
  • Toughness & Vibration Resistance
  • Exceptional Thermal Resistance
  • Comes with High Temperature Reusable Spool
  • Diameter: 1.75mm +/- 0.03mm

Cautions for Use
  • 0.2 mm Nozzle Not Compatible
  • Stainless Steel Nozzle Not Recommended
  • AMS NOT Compatible
  • Dry out before use

Color: Black (72100)
Type:
Size:
Quantity:
$42.99 USD
Discover More Here!
The optimal nozzle for printing carbon fiber reinforced filaments!

Order Info
  • Free shipping on orders over $49
  • Free shipping on orders over $199 to remote areas including Alaska, Hawaii, Puerto Rico, and Guam


Bambu PA6-CF

Bambu PA6-CF is a carbon fiber reinforced PA6 (Nylon 6) filament. The carbon fiber reinforcement provides significantly high stiffness and strength properties in dry environments and maintains exceptional heat resistance and impact resistance. Similar to other Bambu CF Filaments, these outstanding mechanical properties make it an ideal choice for printing fixtures, clamps, automotive and mechanical components and various structural and engineering parts that used in dry environments.

pa6-cf filament pa6-cf filament

Superior Strength and Stiffness

As a new member of Bambu high performance filaments, PA6-CF keeps superior stiffness and strength properties in dry environments, it is perfect for printing load-bearing structural components.

asa filament asa filament
asa filament asa filament
Normal PA-CF PA6-CF Improved %
Strength (Bending Strength - XY, dry state) 128 MPa 151 MPa 18%
Stiffness (Bending Modulus - XY, dry state) 4420 MPa 5460 MPa 24%

Impact & Vibration Resistance

Bambu PA6-CF offers excellent impact resistance, ensuring effective vibration resistance for your prints. It is commonly used to print models that need to withstand impact, collision, and vibration.

pa6-cf pa6-cf

* The prints of PA6-CF will be tougher after putting in humid environment more than 1 day.


Exceptional Thermal Resistance

Filament PLA Basic PETG Basic ABS ASA PC PA6-CF PAHT-CF PET-CF
Heat Deflection Temperature / ℃ (0.45 MPa) 57 ℃ 69 ℃ 87 ℃ 100 ℃ 117 ℃ 186 ℃ 194 ℃ 205 ℃
rfid rfid

Parameters Comparison

Learn more different filaments comparison on Bambu Filament Guide >>

Normal PA6-CF PA6-CF PAHT-CF
Composition Nylon 6, carbon fiber Nylon 6, carbon fiber PA12 and other long-chain PA, carbon fiber
AMS Compatibility NO NO YES
Dry Out Before Use Required Required Required
Printing Speed < 100 mm/s < 100 mm/s < 100 mm/s
Printer Type Enclosure Enclosure Enclosure
Toughness (Impact Strength - XY, dry state) 35.7 kJ/m² 40.3 kJ/m² 57.5 kJ/m²
Toughness (Impact Strength - XY, wet state) 65.4 kJ/m² 57.2 kJ/m² 62.3 kJ/m²
Strength (Bending Strength - XY, dry state) 141 MPa 151 MPa 125 MPa
Strength (Bending Strength - XY, wet state) 67 MPa 95 MPa 115 MPa
Layer Strength (Bending Strength - Z, dry state) 72 MPa 80 MPa 61 MPa
Layer Strength (Bending Strength - Z, wet state) 31 MPa 45 MPa 49 MPa
Stiffness (Bending Modulus - XY, dry state) 4870 MPa 5460 MPa 4230 MPa
Stiffness (Bending Modulus - XY, wet state) 1890 MPa 3560 MPa 3640 MPa
Layer Adhesion (Impact Strength - Z, dry state) 11.6 kJ/m² 15.5 kJ/m² 13.3 kJ/m²
Heat Resistant(HDT, 0.45 MPa) 177 ℃ 186 ℃ 194 ℃
Saturated Water Absorption Rate / % (25 °C,55% RH) 3.80 2.35 0.88


Accessory Compatibility

Recommended Not Recommended
Build Plate Engineering Plate, High Temperature Plate or Textured PEI Plate Cool Plate
Hotend Hardened Steel 0.4 / 0.6 (recommended) / 0.8 mm Hotend with Stainless Steel Nozzle (all size)
Hotend with Hardened Steel Nozzle (0.2 mm)
Glue Glue Stick
Bambu Liquid Glue
/

Recommended Printing Settings
Drying Settings before Printing 80 °C, 8 - 12 h
Printing and Keeping Container's Humidity < 20% RH (Sealed, with Desiccant)
Nozzle Temperature 260 - 290 °C
Bed Temperature (with Glue) 80 - 100 °C
Printing Speed < 100 mm/s
Physical Properties
Density 1.09 g/cm³
Vicat Softening Temperature 212 °C
Heat Deflection Temperature 186 °C
Melting Temperature 223 °C
Melt Index 6.8 ± 0.6 g/10 min
Mechanical Properties
Tensile Strength 102 ± 7 MPa
Breaking Elongation Rate 5.8 ± 1.6 %
Bending Modulus 5460 ± 280 MPa
Bending Strength 151 ± 8 MPa
Impact Strength 40.3 ± 2.5 kJ/m²



Printing Tips

• Drying conditions: 80℃ for 10 hrs. PA6-CF is highly sensitive to humidity. To achieve optimal printing performance, it is recommeded further drying before use and after storage. For more details please refer to: Filament drying instructions on WIKI.

Bambu PA6-CF will experience a decrease in strength and stiffness after absorbing water,making it not recommended for printing models with high requirements for strength, stiffness, and dimensional stability, especially thin and elongated models. The prints of PA6-CF usually become tougher and more resistant to impacts, drops, and collisions when they get damp, you can dampen and soften the prints in advance if the model requires high toughness.

• When printing a model with support, it is necessary to remove the support structure within 2 hours to prevent it from being difficult to remove after being damp and softened. Please dry the prints and let them cool down if it is difficult to remove the support, and then remove the support in time.

• Fully impregnating the surface of the prints with paint, wax and other water-proof coatings can inhibit water absorption and prevent them from becoming soft.